Standard Specification for Aluminum Particle-Filled Basecoat/Organic or Inorganic Topcoat, Corrosion Protective Coatings for Fasteners
| 분야 | |
|---|---|
| 적용범위 | 1.1?This specification covers the basic requirements for a corrosion-resistant coating consisting of an inorganic aluminum particle-filled basecoat and an organic or inorganic topcoat, depending on the specific requirements. 1.2?The coating may be specified with basecoat only, or with the top coated with compatible organic polymer or inorganic topcoats, depending on the specific requirements. 1.3?The basecoat is a water-dilutable slurry containing aluminum particles dispersed in a liquid binder of chromate/phosphate compounds. 1.4?The organic topcoats consist of polymer resins and dispersed pigments and are for service where temperatures do not exceed 230?°C (450?°F). 1.5?The inorganic topcoats consist of ceramic oxide pigments dispersed in a liquid binder of chromate/phosphate compounds and are for service where temperatures do not exceed 645?°C (1200?°F). 1.6?These coatings are applied by conventional dip/spin, dip/drain, or spray methods. 1.7?The coating process does not normally induce hydrogen embrittlement, provided that the parts to be coated have not been subjected to an acid cleaner or pretreatment (see Note 1). Note 1:?Although this coating material contains water, it has a relatively low susceptibility to inducing hydrogen embrittlement in steel parts of tensile strengths equal to or greater than 1000 MPa (approximately RC31). Normal precautions for preparing, descaling, and cleaning steels of these tensile strengths must be observed. An initial stress relief treatment should be considered prior to any chemical treatment or cleaning operation. Acids or other treatments that evolve hydrogen should be avoided. Mechanical cleaning methods may be considered. Some steels are more susceptible to hydrogen embrittlement than others and may also require hydrogen embrittlement relief baking after cleaning but before coating. Since no process can completely guarantee freedom from embrittlement, careful consideration must be given to the entire coating process and the specific steel alloy employed. 1.8?The coating systems defined by this specification can be applied to ferrous alloy steels, aluminum, and ferritic and austenitic stainless steels. 1.9?The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only. 1.10?The following safety hazards caveat pertains only to the test methods portion, Section 6, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.11?This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
| 국제분류(ICS)코드 | |
| 페이지수 | 3 |
| Edition | 23 |
| No. | 표준번호 | 표준명 | 발행일 | 상태 |
|---|---|---|---|---|
| 1 | ASTM F1428-23 | Standard Specification for Aluminum Particle-Filled Basecoat/Organic or Inorganic Topcoat, Corrosion Protective Coatings for Fasteners | 2023-02-01 | 표준 |
| 2 | ASTM F1428-23 REDLINE | Standard Specification for Aluminum Particle-Filled Basecoat/Organic or Inorganic Topcoat, Corrosion Protective Coatings for Fasteners | 2023-02-01 | 표준 |
| 3 | ASTM F1428-92(2017) | Standard Specification for Aluminum Particle-Filled Basecoat/Organic or Inorganic Topcoat, Corrosion Protective Coatings for Fasteners | 2017-12-01 | 구판 |
| 4 | ASTM F1428-92(2011) | Standard Specification for Aluminum Particle-Filled Basecoat/Organic or Inorganic Topcoat, Corrosion Protective Coatings for Fasteners | 2011-11-01 | 구판 |
| 5 | ASTM F1428-92(2005) | Standard Specification for Aluminum Particle-Filled Basecoat/Organic or Inorganic Topcoat, Corrosion Protective Coatings for Fasteners | 2005-05-01 | 구판 |
| 6 | ASTM F1428-92(1999) | Standard Specification for Aluminum Particle-Filled Basecoat/Organic or Inorganic Topcoat, Corrosion Protective Coatings for Fasteners | 1999-05-10 | 구판 |
관련상품이 존재하지 않습니다.
ASTM D3359-23 REDLINE - Standard Test Methods for Rating Adhesion by Tape Test 상세보기
ASTM B633-23 REDLINE - Standard Specification for Electrodeposited Coatings of Zinc on Iron and Steel 상세보기
ASTM B487-20 REDLINE - Standard Test Method for Measurement of Metal and Oxide Coating Thickness by Microscopical Examination of Cross Section 상세보기
ASTM B602-21 - Standard Guide for Attribute Sampling of Metallic and Inorganic Coatings 상세보기
ASTM D5894-21 - Standard Practice for Cyclic Salt Fog/UV Exposure of Painted Metal, (Alternating Exposures in a Fog/Dry Cabinet and a UV/Condensation Cabinet) 상세보기
IEC TS 63134:2020 - Active assisted living (AAL) use cases 상세보기
IEC 60034-5:2020 RLV - Rotating electrical machines - Part 5: Degrees of protection provided by the integral design of rotating electrical machines (IP code) - Classification 상세보기
KS B ISO TS 25740-1 - 에스컬레이터 및 무빙워크에 대한 안전요건 — 제1부: 세계공통 필수 안전요건(GESRs) 상세보기
KS B ISO TS 8100-21 - 승객 및 화물 운송용 엘리베이터 —제21부: 세계공통 필수안전요건(GESRs)을 충족하는 세계공통 안전 파라미터(GSPs) 상세보기
KS C IEC TS 62872 - 산업 시설과 스마트 그리드 사이의 산업 공정 측정, 제어 및 자동화 시스템 인터페이스 상세보기
KS표준
핸드북