ASTM C618-12a Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete

관심표준 등록 : 표준업데이트 시 알림을 받을 수 있습니다.

PDF : 직접 파일 다운로드 및 인쇄 (마이페이지 확인)

PRINT : 인쇄본 우편발송, 2~3일 소요(PDF파일 미제공)

구판 판매

ASTM C618-12a

Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete

- 발행일 : 2012-12-15
- 발행기관 : ASTM

언어	제공형태	판매가격	선택
영어	PDF	128,900원
영어	PRINT	128,900원

장바구니 담기

상품이 장바구니에 담겼습니다.

장바구니로 이동

상세정보

분야

04.02 : 콘크리트 및 골재

적용범위

1.1 This specification covers coal fly ash and raw or calcined natural pozzolan for use in concrete where cementitious or pozzolanic action, or both, is desired, or where other properties normally attributed to fly ash or pozzolans may be desired, or where both objectives are to be achieved .

Note 1—Finely divided materials may tend to reduce the entrained air content of concrete. Hence, if a fly ash or natural pozzolan is added to any concrete for which entrainment of air is specified, provision should be made to ensure that the specified air content is maintained by air content tests and by use of additional air-entraining admixture or use of an air-entraining admixture in combination with air-entraining hydraulic cement.

TABLE 1 Chemical Requirements

	Class
	N	F	C
Silicon dioxide (SiO₂) plus aluminum oxide (Al₂O₃) plus iron oxide (Fe₂O₃), min, %	70.0	70.0	50.0
Sulfur trioxide (SO₃), max, %	4.0	5.0	5.0
Moisture content, max, %	3.0	3.0	3.0
Loss on ignition, max, %	10.0	6.0^A	6.0

^A The use of Class F pozzolan containing up to 12.0 % loss on ignition may be approved by the user if either acceptable performance records or laboratory test results are made available.

TABLE 2 Physical Requirements

	Class
	N	F	C
Fineness:
Amount retained when wet-sieved on 45 μm (No. 325) sieve, max, %	34	34	34
Strength activity index: ^A
With portland cement, at 7 days, min, percent of control	75^B	75^B	75^B
With portland cement, at 28 days, min, percent of control	75^B	75^B	75^B
Water requirement, max, percent of control	115	105	105
Soundness: ^C
Autoclave expansion or contraction, max, %	0.8	0.8	0.8
Uniformity requirements:
The density and fineness of individual samples shall not vary from the average established by the ten preceding tests, or by all preceding tests if the number is less than ten, by more than:
Density, max variation from average, %	5	5	5
Percent retained on 45-μm (No. 325), max variation, percentage points from average	5	5	5

^A The strength activity index with portland cement is not to be considered a measure of the compressive strength of concrete containing the fly ash or natural pozzolan. The mass of fly ash or natural pozzolan specified for the test to determine the strength activity index with portland cement is not considered to be the proportion recommended for the concrete to be used in the work. The optimum amount of fly ash or natural pozzolan for any specific project is determined by the required properties of the concrete and other constituents of the concrete and is to be established by testing. Strength activity index with portland cement is a measure of reactivity with a given cement and is subject to variation depending on the source of both the fly ash or natural pozzolan and the cement.

^B Meeting the 7 day or 28 day strength activity index will indicate specification compliance.

^C If the fly ash or natural pozzolan will constitute more than 20 % by mass of the cementitious material in the project mixture, the test specimens for autoclave expansion shall contain that anticipated percentage. Excessive autoclave expansion is highly significant in cases where water to cementitious material ratios are low, for example, in block or shotcrete mixtures.

TABLE 3 Supplementary Optional Physical Requirements

Note 1—These optional requirements apply only when specifically requested.

	Class
	N	F	C
Increase of drying shrinkage of mortar bars at 28 days, max, difference, in %, over control^A	0.03	0.03	0.03
Uniformity Requirements:
In addition, when air-entraining concrete is specified, the quantity of air- entraining agent required to produce an air content of 18.0 vol % of mortar shall not vary from the average established by the ten preceding tests or by all preceding tests if less than ten, by more than, %	20	20	20
Effectiveness in Controlling Alkali-Silica Reaction:^B
Expansion of test mixture as percentage of low-alkali cement control, at 14 days, max, %	100	100	100
Effectiveness in Contributing to Sulfate Resistance:^C
Procedure A:
Expansion of test mixture:
For moderate sulfate exposure after 6 months exposure, max, %	0.10	0.10	0.10
For high sulfate exposure after 6 months exposure, max, %	0.05	0.05	0.05
Procedure B:
Expansion of test mixture as a percentage of sulfate resistance cement control after at least 6 months exposure, max,%	100	100	100

^A Determination of compliance or noncompliance with the requirement relating to increase in drying shrinkage will be made only at the request of the purchaser.

^B Fly ash or natural pozzolans meeting this requirement are considered as effective in controlling alkali silica reactions as the use of the low-alkali control cement used in the evaluation. However, the fly ash or natural pozzolan shall be considered effective only when used at percentages by mass of the total cementitious material equal to or exceeding that used in the tests and when the alkali content of the cement to be used does not exceed that used in the tests by more than 0.05 %. See Appendix XI, Test Methods C311.

^C Fly ash or natural pozzolan shall be considered effective only when the fly ash or natural pozzolan is used at percentages, by mass, of the total cementitious material within 2 % of those that are successful in the test mixtures or between two percentages that are successful, and when the C₃A content of the project cement is less than, or equal to, that which was used in the test mixtures. See Appendix X2 of Test Method C311.

1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

1.3 The text of this standard references notes and footnotes, which provide explanatory information. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.

국제분류(ICS)코드

페이지수

Edition

12a

이력정보

No.	표준번호	표준명	발행일	상태
1	ASTM C618-23	Standard Specification for Coal Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2023-03-01	구판
2	ASTM C618-23e1	Standard Specification for Coal Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2023-03-01	표준
3	ASTM C618-22	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2022-08-01	구판
4	ASTM C618-22 REDLINE	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2022-08-01	구판
5	ASTM C618-19	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2019-01-01	구판
6	ASTM C618-19 REDLINE	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2019-01-01	구판
7	ASTM C618-17a	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2017-12-15	구판
8	ASTM C618-17a REDLINE	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2017-12-15	구판
9	ASTM C618-17	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2017-10-01	구판
10	ASTM C618-15	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2015-08-01	구판
11	ASTM C618-12a	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2012-12-15	구판
12	ASTM C618-12	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2012-02-01	구판
13	ASTM C618-08a	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2008-10-01	구판
14	ASTM C618-08	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2008-03-01	구판
15	ASTM C618-05	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2005-07-01	구판
16	ASTM C618-03	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete	2003-01-10	구판
17	JASO C618-03	Test procedures for high speed uniformity of tyre/wheel assembly	2003-01-01	표준
18	ASTM C618-02	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use as a Mineral Admixture in Concrete	2002-12-10	구판
19	ASTM C618-00	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use as a Mineral Admixture in Concrete	2001-08-10	구판
20	ASTM C618-01	Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use as a Mineral Admixture in Concrete	2001-08-10	구판
21	ASTM C618-78	Standard Specification for Fly Ash And Raw Or Calcined Natural Pozzolan For Use As A Mineral Admixture In Portland Cement Concrete		구판

관련상품

관련상품이 존재하지 않습니다.
다른 사람이 함께 구입한 상품

함께 구입한 상품이 존재하지 않습니다.
추천 상품

IEC TS 63134:2020 - Active assisted living (AAL) use cases 상세보기

IEC 60034-5:2020 RLV - Rotating electrical machines - Part 5: Degrees of protection provided by the integral design of rotating electrical machines (IP code) - Classification 상세보기

KS B ISO TS 25740-1 - 에스컬레이터 및 무빙워크에 대한 안전요건 — 제1부: 세계공통 필수 안전요건(GESRs) 상세보기

KS B ISO TS 8100-21 - 승객 및 화물 운송용 엘리베이터 —제21부: 세계공통 필수안전요건(GESRs)을 충족하는 세계공통 안전 파라미터(GSPs) 상세보기

KS C IEC TS 62872 - 산업 시설과 스마트 그리드 사이의 산업 공정 측정, 제어 및 자동화 시스템 인터페이스 상세보기

해외표준

ASTM C618-12a

상세정보

이력정보

관련상품

다른 사람이 함께 구입한 상품

추천 상품

전체서비스 보기